مقاله A Study on the Effect of Cathodic Polarization in the Pitting Corrosion of AA5083-H321 Aluminum-Magnesium Alloy in a 3.5% NaCI Solution

توجه : به همراه فایل word این محصول فایل پاورپوینت (PowerPoint) و اسلاید های آن به صورت هدیه ارائه خواهد شد

  مقاله A Study on the Effect of Cathodic Polarization in the Pitting Corrosion of AA5083-H321 Aluminum-Magnesium Alloy in a 3.5% NaCI Solution دارای ۱۴ صفحه می باشد و دارای تنظیمات در microsoft word می باشد و آماده پرینت یا چاپ است

فایل ورد مقاله A Study on the Effect of Cathodic Polarization in the Pitting Corrosion of AA5083-H321 Aluminum-Magnesium Alloy in a 3.5% NaCI Solution  کاملا فرمت بندی و تنظیم شده در استاندارد دانشگاه  و مراکز دولتی می باشد.

توجه : در صورت  مشاهده  بهم ریختگی احتمالی در متون زیر ،دلیل ان کپی کردن این مطالب از داخل فایل ورد می باشد و در فایل اصلی مقاله A Study on the Effect of Cathodic Polarization in the Pitting Corrosion of AA5083-H321 Aluminum-Magnesium Alloy in a 3.5% NaCI Solution،به هیچ وجه بهم ریختگی وجود ندارد

بخشی از متن مقاله A Study on the Effect of Cathodic Polarization in the Pitting Corrosion of AA5083-H321 Aluminum-Magnesium Alloy in a 3.5% NaCI Solution :

تعداد صفحات:۱۴

چکیده:

Cathodic protection of aluminum-magnesium alloy AAS083-H321 as a suitable material for construction of high speed boats, submarines, desalination systems etc., is one of the proposed methods for their protection against pitting corrosion. In this research, the cathodic polarization of this alloy has been studied in a 3.S% sodium chloride solution at- 0.9, -1, -1.1 and -1.2 VSCB. The electrochemical behavior of the surmce was investigated by EIS and DC methods. Morphological changes on the surface and the cross section of the samples were studied using scanning electron microscope (SEM) and EDAX analyzer. The results showed that at all potentials. pits density on the surfilce increases with the decrease of cathodic potential. Decreasing the potential accelerates the non-ideal behavior of the
double layer capacitance at the interfil.ce of the oxide layer/solution. This results from the deepening of pits during cathodic polarization of the above-mentioned alloys. Finally, cathodic protection of these alloys is impossible while they are in stationary conditions.