مقاله Carbide Precipitation in the Microstructures of Austempered Ductile Irons Containing 0.48% and 4.88% Al

توجه : به همراه فایل word این محصول فایل پاورپوینت (PowerPoint) و اسلاید های آن به صورت هدیه ارائه خواهد شد

 مقاله Carbide Precipitation in the Microstructures of Austempered Ductile Irons Containing 0.48% and 4.88% Al دارای ۱۳ صفحه می باشد و دارای تنظیمات در microsoft word می باشد و آماده پرینت یا چاپ است

فایل ورد مقاله Carbide Precipitation in the Microstructures of Austempered Ductile Irons Containing 0.48% and 4.88% Al  کاملا فرمت بندی و تنظیم شده در استاندارد دانشگاه  و مراکز دولتی می باشد.

توجه : در صورت  مشاهده  بهم ریختگی احتمالی در متون زیر ،دلیل ان کپی کردن این مطالب از داخل فایل ورد می باشد و در فایل اصلی مقاله Carbide Precipitation in the Microstructures of Austempered Ductile Irons Containing 0.48% and 4.88% Al،به هیچ وجه بهم ریختگی وجود ندارد

بخشی از متن مقاله Carbide Precipitation in the Microstructures of Austempered Ductile Irons Containing 0.48% and 4.88% Al :

سال انتشار : ۲۰۰۵

تعداد صفحات :۱۳

The influence of aluminium on the microstructure of austempered ductile cast iron (ADI) has been studied. The presence of well distributed graphite in the matrix, and a relatively high volume fraction of retained austenite are responsible for the good mechanical properties of the Aluminium alloyed austempered ductile irons including excellent wear resistance, higher resistance to thermal shock, better graphitising tendency and higher resistance to oxidation at high temperatures. A number of specimens of different composition have been made by green sand-casting and gravity die-casting. The transformation to a bainitic microstructure during austempering under different conditions was then examined for the most successful experimental casts. Austenitising temperature of 920°C, and austempering temperatures of 350°C at different holding times have been used. Microstructures have been examined by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Furthermore, it was found that isothermal transformation at 350°C for different soaking times gave a typical bainitic microstructure. Extension of isothermal transformation time leads to precipitation of carbides which also depends on the Al concentration.