مقاله Investigation of oxidation behavior and Thermal spray of mechanically milled CoNiCrAlY–YSZ powders


در حال بارگذاری
مقاله Investigation of oxidation behavior and Thermal spray of mechanically milled CoNiCrAlY–YSZ powders
23 اکتبر 2022
فایل ورد و پاورپوینت
2120
3 بازدید
۹۷,۷۰۰ تومان
خرید

توجه : به همراه فایل word این محصول فایل پاورپوینت (PowerPoint) و اسلاید های آن به صورت هدیه ارائه خواهد شد

 مقاله Investigation of oxidation behavior and Thermal spray of mechanically milled CoNiCrAlY–YSZ powders دارای ۱۳ صفحه می باشد و دارای تنظیمات در microsoft word می باشد و آماده پرینت یا چاپ است

فایل ورد مقاله Investigation of oxidation behavior and Thermal spray of mechanically milled CoNiCrAlY–YSZ powders  کاملا فرمت بندی و تنظیم شده در استاندارد دانشگاه  و مراکز دولتی می باشد.

توجه : در صورت  مشاهده  بهم ریختگی احتمالی در متون زیر ،دلیل ان کپی کردن این مطالب از داخل فایل ورد می باشد و در فایل اصلی مقاله Investigation of oxidation behavior and Thermal spray of mechanically milled CoNiCrAlY–YSZ powders،به هیچ وجه بهم ریختگی وجود ندارد

بخشی از متن مقاله Investigation of oxidation behavior and Thermal spray of mechanically milled CoNiCrAlY–YSZ powders :

سال انتشار : ۲۰۱۵

تعداد صفحات :۱۳

In this study, the effects of mechanical milling and YSZ reinforcing on oxidation behavior of CoNiCrAlY coatings were investigated. Various amounts of YSZ particles (0%, 5%, 10% and 15 wt.%) were mixed with commercial CoNiCrAlY powder and milled for 24 hrs. Then, the mechanically milled and commercial powders were deposited on Inconel 617 substrate using High Velocity Oxygen-Fuel (HVOF) process. Freestanding bodies of nanostructured and conventional HVOF CoNiCrAlY coatings were oxidized at 1000 °C for different times to form the thermally grown oxide layer. X-ray diffraction analysis, scanning electron microscopy and X-ray mapping were used to analyze the scales formed on the surface of the oxidized samples. The results showed that nanostructured coatings exhibited higher porosity due to undesirable morphology of feedstock powders. This factor accelerated diffusion rate of oxygen into coating body. On the other hand, undesireable oxidation of nanostructured particles during spraying leads to increase in the oxidation rate of coatings.